ÖNORM EN ISO 16701
Ausgabedatum: 2008 09 01
Korrosion von Metallen und Legierungen - Korrosion in künstlicher Atmosphäre - Schnellkorrosionsprüfungen unter zyklischer Einwirkung von Feuchte und intermittierendem Versprühen einer Salzlösung unter kontrollierten Bedingungen (ISO 16701:2003)
This standard defines an accelerated corrosion test method to be used in assessing the corrosion resistance of metals in environments where there is a significant influen...
Weiterlesen
ZURÜCKGEZOGEN
: 2015 09 15
Herausgeber:
Austrian Standards International
Format:
Digital | 19 Seiten
Sprache:
Deutsch
| Englisch
| Download DE/EN
Aktuell Gültig:
Standards mitgestalten:
ICS
This standard defines an accelerated corrosion test method to be used in assessing the corrosion resistance of metals in environments where there is a significant influence of chloride ions, mainly
as sodium chloride from a marine source or road de-icing salt.
This standard specifies the test apparatus and test procedure to be used in conducting the accelerated corrosion test to simulate, in a very controlled way, atmospheric corrosion conditions. In this standard, the term ¿metal¿ includes metallic materials with or without corrosion protection. The accelerated laboratory corrosion test applies to metals and their alloys; metallic coatings (anodic and cathodic); chemical conversion coatings; organic coatings on metals. The method is especially suitable for comparative testing in the optimization of surface treatment systems.
ÖNORM EN ISO 16701
2015 09 15
Korrosion von Metallen und Legierungen - Korrosion in künstlicher Atmosphäre - Beschleunigte Korrosi...
Norm
ÖNORM EN ISO 16701
2008 09 01
Korrosion von Metallen und Legierungen - Korrosion in künstlicher Atmosphäre - Schnellkorrosionsprüf...
Norm
↖
Schlussentwurf
ISO/FDIS 4628-1
Ausgabedatum :
2015 09 17
Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 1: General introduction and designation system
Norm
ISO 4628-1:2003
Ausgabedatum :
2003 09 10
Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 1: General introduction and designation system
Schlussentwurf
ISO/FDIS 4628-2
Ausgabedatum :
2015 09 17
Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 2: Assessment of degree of blistering
Norm
ISO 4628-2:2003
Ausgabedatum :
2003 09 10
Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 2: Assessment of degree of blistering
Schlussentwurf
ISO/FDIS 4628-4
Ausgabedatum :
2015 09 17
Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 4: Assessment of degree of cracking
Norm
ISO 4628-4:2003
Ausgabedatum :
2003 09 12
Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 4: Assessment of degree of cracking
Schlussentwurf
ISO/FDIS 4628-5
Ausgabedatum :
2015 09 17
Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 5: Assessment of degree of flaking
Norm
ISO 4628-5:2003
Ausgabedatum :
2003 09 12
Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 5: Assessment of degree of flaking
Norm
ISO 8407:2009
Ausgabedatum :
2009 10 27
Corrosion of metals and alloys — Removal of corrosion products from corrosion test specimens
Norm
ISO 4628-1:2016
Ausgabedatum :
2016 01 12
Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 1: General introduction and designation system
Norm
ISO 4628-2:2016
Ausgabedatum :
2016 01 12
Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 2: Assessment of degree of blistering
Norm
ISO 4628-4:2016
Ausgabedatum :
2016 01 12
Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 4: Assessment of degree of cracking
Norm
ISO 4628-5:2016
Ausgabedatum :
2016 01 12
Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 5: Assessment of degree of flaking
Norm
ISO 8407:2021
Ausgabedatum :
2021 01 04
Corrosion of metals and alloys — Removal of corrosion products from corrosion test specimens
Norm
ISO 10289:1999
Ausgabedatum :
1999 11 18
Methods for corrosion testing of metallic and other inorganic coatings on metallic substrates — Rating of test specimens and manufactured articles subjected to corrosion tests
Norm
ÖNORM EN ISO 16701
Ausgabedatum :
2015 09 15
Korrosion von Metallen und Legierungen - Korrosion in künstlicher Atmosphäre - Beschleunigte Korrosionsprüfungen unter zyklischer Einwirkung von Feuchte und intermittierendem Versprühen einer Salzlösung unter kontrollierten Bedingungen (ISO 16701:2015)
Norm
ISO 16701:2003
Ausgabedatum :
2003 11 25
Corrosion of metals and alloys — Corrosion in artificial atmosphere — Accelerated corrosion test involving exposure under controlled conditions of humidity cycling and intermittent spraying of a salt solution